| 規格級別 | 擠出 | 加工級別 | 擠出級,滾塑級 | 特性級別 | 高強度 |
在線訂購支持
在線訂購說明
保障消費者權益，真正做到正品交易，杜絕假冒偽劣產品
021-58958519 13061808058(蔣先生) 13424755533(趙先生)
聯系上海松翰
| 021-58958519 | |
| 13061808058(蔣先生) | |
| 13424755533(趙先生) | |
| |
|
|
產品簡述
備注
備注:顆粒料
詳細數據
訂購指南
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 物理性能 | 比重 | ASTM D792 | 1.20 | g/cm3; | |
| 熔流率 | 300°C/1.2 kg | ASTM D1238 | 3.0 | g/10 min | |
| 收縮率 | 流動 | ASTM D955 | 0.50-0.70 | % | |
| 吸水率 | 23°C, 24 hr | ASTM D570 | 0.15 | % | |
| 平衡, 23°C, 50% RH | ASTM D570 | 0.32 | % | ||
| 洛氏硬度 | M 計秤 | ASTM D785 | 74 | ||
| R 計秤 | ASTM D785 | 118 | |||
| 機械性能 | 拉伸模量 | ASTM D638 | 2480 | MPa | |
| 抗張強度 | 屈服, 23°C 2 | ASTM D638 | 60.0 | MPa | |
| 斷裂 | ASTM D638 | 72.4 | MPa | ||
| 伸長率 | 屈服 | ASTM D638 | 6.0 | % | |
| 斷裂 | ASTM D638 | 150 | % | ||
| 彎曲模量 | ASTM D790 | 2410 | MPa | ||
| 彎曲強度 | ASTM D790 | 96.5 | MPa | ||
| 耐磨耗性 | Change in Haze (1000 g; CS-10 F wheel; 500 cycles) |
ASTM D1044 | 45 | % | |
| 懸壁梁缺口沖擊強度 3 | 23°C, 3.18 mm | ASTM D256 | 960 | J/m | |
| 無缺口懸臂梁沖擊 | 23°C | ASTM D256 | 無斷裂 | ||
| 裝有測量儀表的落鏢沖擊 4 | 23°C, 3.18 mm, Total Energy | ASTM D3763 | 93.8 | J | |
| 熱性能 | 熱變形溫度 | 0.45 MPa, 退火 , 4.00 mm | ASTM D648 | 146 | °C |
| 1.8 MPa,未退火 , 4.00 mm | ASTM D648 | 132 | °C | ||
| 1.8 MPa, 退火 , 4.00 mm | ASTM D648 | 143 | °C | ||
| 維卡軟化溫度 | |
ASTM D1525 5 | 151 | °C | |
| 球壓溫度 6 | IEC 60598-1 | >125 | °C | ||
| 線形膨脹系數 | 流動 (-40 到 82°C) | ASTM D696 | 0.000068 | cm/cm/°C | |
| 電氣性能 | 體積電阻率 7 | 23°C | ASTM D257 | 2.0E+17 | ohm·cm |
| 介電強度 | ASTM D149 | 17 | kV/mm | ||
| 介電常數 | 60 Hz | ASTM D150 | 3.00 | ||
| 耗散因數 | 60 Hz | ASTM D150 | 0.0010 | ||
| 漏電起痕指數 | 2.00 mm | IEC 60112 | 250 | V | |
| 其它 | UL 阻燃等級 6 |
3.00 mm
|
UL 94 | HB | |
|
0.500 mm
|
UL 94 | V-2 | |||
|
1.60mm
|
UL 94 | V-2 | |||
| 熱燈絲點火溫度 | 2.00 mm, 5.0 sec | EC 60695-2-13 | 850 | °C | |
| 極限氧指數 6 | ASTM D2863 | 26 | % | ||
| UL 檔案號 | E93278 | ||||
| 平均燃燒程度 6 | ASTM D635 | 3 | cm | ||
| 光學性能 | 折射率 | ASTM D542 | 1.586 | ||
| 透射率 | ASTM D1003 | 89.0 | % | ||
| 霧度 | ASTM D1003 | 0.70-1.5 | % | ||
PC/韓國LG-DOW/300-3 包裝圖片
版權所有 ? www.ykgangcai.com All Rights Reserved